This table is provided as an information service by Diversified Enterprises.

This table highlights polar/dispersion and acid—base breakouts of surface free energy, as well as Hansen Solubility Parameters and radius of interaction, for a variety of polymers. For all columns except polymer name, CAS #, and total Hansen Solubility Parameter (δ) the first row of data for each material is the average of surveyed values; the second row shows the standard deviation, with the number of data points (n) in parentheses. For n = 1, no standard deviation figure is shown. Click on any column's footnote for details. Click on any polymer name for original research results. An analogous table, which includes contact angle data, can be seen here. Comments on methodology and the like can be found here.

This table can be sorted by column — just click on the column header as desired to re-order this printable table. Click on any footnote for additional information.

Some print software will automatically scale this page so that it prints well with “portrait” orientation. If your printer doesn't have this feature, you will want to change your print set-up to “landscape” orientation prior to printing.

print this sort order (table and references only - will open in new browser window)

Surface Free Energy Components by Polar/Dispersion and Acid—Base Analyses; and Hansen Solubility Parameters for Various Polymers

  Polar/Dispersion Acid-Base Hansen Parameters
Name(1)
ascendingdescending
CAS #(2)
ascending descending
γS(3)
ascending descending
γSd(4)
ascending descending
γSP(5)
ascending descending
γS(6)
ascending descending
γSLW(7)
ascending descending
γSAB(8)
ascending descending
γS+ (9)
ascending descending
γS- (10)
ascending descending
δ(11)
ascending descending
δD(12)
ascending descending
δP(13)
ascending descending
δH(14)
ascending descending
Ro(15)
ascending descending
Amorphous fluoropolymer (Teflon AF) - - - - - - - - - - - - - -
 
Aramid (Kevlar) 26125-61-1 - - - - - - - - - - - - -
 
Cellulose acetate butyrate (CAB) 9004-36-8 - - - - - - - - 22.2 17.2 13.8 2.8 12.6
  -(1) -(1) -(1) -(1)
Cellulose triacetate 9012-09-3 - - - - - - - - - - - - -
 
Eicosane 112-95-8 - - - - - - - - - - - - -
 
Ethyl cellulose 9004-57-3 - - - 28.6 27.4 1.2 0.04 8.6 20.4 19.0 5.6 4.9 7.9
  -(1) -(1) -(1) -(1) -(1) 1.56(2) 1.84(2) 1.41(2) 2.83(2)
Nafion 31175-20-9 - - - - - - - - - - - - -
 
Nitrocellulose (cellulose nitrate) 9004-70-0 - - - 45.1 44.8 0.3 0.01 13.3 23.5 16.2 14.1 9.5 10.7
  0.14(2) 0.21(2) 0.35(2) 0.01(2) 3.75(2) 1.06(2) 0.85(2) 1.06(2) 1.13(2)
Nylon 6,10 9008-66-6 - - - - - - - - - - - - -
 
Nylon 7,7 - - - - - - - - - - - - - -
 
Nylon 8,8 - - - - - - - - - - - - - -
 
Nylon 9,9 - - - - - - - - - - - - - -
 
Nylon 10,10 - - - - - - - - - - - - - -
 
Nylon 11 25587-80-8 - - - - - - - - 20.5 17.0 4.4 10.6 5.1
  -(1) -(1) -(1) -(1)
Phenoxy resin 26402-79-9 - - - - - - - - - - - - -
 
Polyacrylonitrile (PAN) 25014-41-9 - - - - - - - - 27.4 21.7 14.1 9.1 10.9
  -(1) -(1) -(1) -(1)
Polybenzyl methacrylate 25085-83-0 - - - - - - - - - - - - -
 
Polyetherimide (PEI) 61128-46-9 - - - - - - - - 19.8 17.7 6.0 6.4 4.8
  1.07(5) 1.14(5) 2.43(5) 1.70(5)
Poly 2-ethylhexyl methacrylate 25719-51-1 - - - - - - - - - - - - -
 
Poly(heptafluoroisopropyl acrylate) - - - - - - - - - - - - - -
 
Poly(heptafluoroisopropyl methacrylate) - - - - - - - - - - - - - -
 
Poly(2-hydroxyethyl methacrylate) 24249-16-5 - - - - - - - - - - - - -
 
Polyisoprene (PIP) 9003-31-0 - - - - - - - - 18.4 18.1 2.4 2.3 10.3
  2.32(3) 1.40(3) 2.66(3) 3.40(3)
Polylauryl methacrylate 25719-52-2 - - - - - - - - - - - - -
 
Polymethacrylonitrile (PMAN) 25067-61-2 - - - - - - - - 23.7 17.2 14.4 7.6 3.8
  -(1) -(1) -(1) -(1)
Poly(4-methyl pentene-1) - - - - - - - - - - - - - -
 
Poly a-methyl styrene 25014-31-7 - - - - - - - - - - - - -
 
Polymethylphenylsiloxane 9005-12-3 - - - - - - - - - - - - -
 
Polymethylphenylsilylene - - - - - - - - - - - - - -
 
Poly(nonafluoroisobutyl acrylate) - - - - - - - - - - - - - -
 
Polyoctyl methacrylate - - - - - - - - - - - - - -
 
Polyphenyl methacrylate - - - - - - - - - - - - - -
 
Poly(phosphazene) - - - - - - - - - - - - - -
 
Poly n-propyl methacrylate 2210-79-9 - - - - - - - - - - - - -
 
Polystearyl methacrylate 25639-21-8 - - - - - - - - - - - - -
 
Polyvinyl alcohol (PVOH) 25213-24-5 - - - 42.0 42.0 0.0 0.0 37.0 25.2 14.7 14.1 14.9 10.5
  -(1) -(1) -(1) -(1) -(1) 2.51(4) 2.13(4) 2.18(4) 1.38(4)
Polyvinyl butyral 63148-65-2 - - - - - - - - 24.6 19.1 9.5 12.2 10.0
  0.92(3) 4.50(3) 1.65(3) 1.53(3)
Polyvinyl ethyl ether (polyethoxyethylene) 25104-37-4 - - - - - - - - - - - - -
 
Polyvinyl formal 63450-15-7 - - - - - - - - - - - - -
 
Polyvinyl pyrrolidone (PVP) 9003-39-8 - - - 46.0 43.4 2.6 0.2 22.5 - - - - -
  3.61(2) 0.00(2) 3.61(2) 0.28(2) 10.2(2)
Polybutadiene 9003-17-2 - - - - - - - - 18.0 17.5 2.3 3.4 6.6
  -(1) -(1) -(1) -(1)
Poly(dimethylaminoethylmethacrylate) - - - - - - - - - - - - - -
 
Polyepichlorohydrin 24969-06-0 - - - - - - - - - - - - -
 
Paraffin 8002-74-2 28.1 28.1 0.0 - - - - - - - - - -
  3.71(7) 3.71(7) 0.00(7)
Polyisobutylene (PIB, butyl (rubber) 9003-27-4 33.6 33.6 0.0 25.0 25.0 0.0 0.0 0.0 17.1 16.4 1.7 4.7 7.9
  -(1) -(1) -(1) -(1) -(1) -(1) -(1) -(1) 1.26(6) 2.15(6) 2.08(6) 2.46(6)
Hexatriacontane 630-06-8 23.7 23.6 0.1 - - - - - - - - - -
  6.71(3) 6.78(3) 0.12(3)
Polypropylene glycol (PPG, polypropylene oxide) 25322-69-4 31.7 31.3 0.4 - - - - - - - - - -
  -(1) -(1) -(1)
Polyxylylene (parylene) - 46.3 45.7 0.6 - - - - - - - - - -
  -(1) -(1) -(1)
Poly(hexachlorobutadiene) - 41.5 40.7 0.8 - - - - - - - - - -
  -(1) -(1) -(1)
Polytetrafluoroethylene (PTFE) 9002-84-0 22.2 21.3 0.9 20.8 19.9 0.9 0.1 1.6 16.7 16.2 1.8 3.4 3.9
  2.54(9) 2.71(10) 0.96(9) 0.99(2) 0.35(2) 1.34(2) 0.20(2) 2.26(2) -(1) -(1) -(1) -(1)
Polyvinyl hexadecanoate - 30.9 29.8 1.1 - - - - - - - - - -
  -(1) -(1) -(1)
Poly 2-ethylhexyl acrylate 9003-77-4 30.1 28.9 1.3 - - - - - - - - - -
  0.90(3) 1.57(3) 0.78(3)
Poly(hexafluoropropylene) - 14.9 13.6 1.3 - - - - - - - - - -
  2.10(3) 1.48(3) 1.55(3)
Polyvinyl dodecanoate - 29.1 27.8 1.3 - - - - - - - - - -
  -(1) -(1) -(1)
Polydimethylsiloxane (PDMS) 9016-00-6 205 19.2 1.3 - - - - - - - - - -
  1.16(6) 1.48(6) 0.66(6)
Polyethylene (PE) 9002-88-4 34.2 32.8 1.4 31.7 31.5 0.2 0.1 0.9 17.6 16.8 3.8 3.8 6.6
  2.45(19) 2.89(19) 1.73(19) 2.86(10) 2.93(10) 0.27(10) 0.19(10) 1.39(10) 0.88(7) 1.94(7) 2.52(7) 2.84(7)
Poly(heptadecafluorooctyl methacrylate) - 15.3 13.9 1.4 - - - - - - - - - -
  -(1) -(1) -(1)
Polyvinyl decanoate - 28.9 27.1 1.8 - - - - - - - - - -
  -(1) -(1) -(1)
Polydiethylsiloxane (PDES) 63148-61-8 25.7 23.8 1.9 - - - - - - - - - -
  -(1) -(1) -(1)
Polyvinyl octanoate - 28.7 26.5 2.2 - - - - - - - - - -
  -(1) -(1) -(1)
Thermoplastic polyolefin (TPO) - 30.9 28.5 2.3 - - - - - - - - - -
  3.45(11) 2.80(11) 3.63(11)
Polypropylene (PP) (a) 30.1 27.7 2.4 32.0 31.7 0.3 0.2 0.4 18.0 17.7 2.9 1.2 6.2
  2.42(11) 2.46(11) 2.45(11) 3.99(8) 3.56(8) 0.76(8) 0.45(8) 0.76(8) 0.46(2) 2.80(2) 1.71(2) 1.76(2)
Poly(hexyl methacrylate) 25087-17-6 30.0 27.6 2.5 - - - - - - - - - -
  0.00(2) 0.78(2) 0.78(2)
Fluorinated ethylene polypropylene (FEP) 25067-11-2 19.9 17.1 2.8 17.9 17.9 0.0 0.0 0.0 19.6 19.0 4.0 3.0 4.0
  2.90(3) 2.66(3) 2.51(3) -(1) -(1) -(1) -(1) -(1) -(1) -(1) -(1) -(1)
Polyphenylene sulfide (PPS) 26125-40-6 46.8 44.0 2.8 - - - - - 19.8 18.7 5.3 3.7 6.7
  3.29(3) 3.50(3) 0.71(3) -(1) -(1) -(1) -(1)
Polyvinyl chloride (PVC) 9002-86-2 40.1 37.4 2.8 39.8 38.7 1.0 0.1 3.1 20.0 16.8 8.9 6.1 8.5
  3.80(9) 3.93(10) 2.36(9) 4.76(6) 4.33(6) 0.96(6) 0.15(6) 2.31(6) 1.65(5) 1.95(5) 1.78(5) 3.94(5)
Ethyl methacrylate (EMA) 97-63-2 42.0 38.8 3.2 - - - - - - - - - -
  1.06(2) 0.42(2) 0.64(2)
Polyacetylene (polyethyne) - 51.5 48.2 3.4 - - - - - - - - - -
  0.71(2) 1.77(2) 1.06(2)
Poly n-butyl acrylate 9003-49-0 32.2 28.6 3.6 - - - - - - - - -
  2.12(2) 2.55(2) 0.42(2)
Polyvinyl hexanoate - 28.9 25.1 3.8 - - - - - - - - - -
  -(1) -(1) -(1)
Poly t-butyl methacrylate (PtBMA) 25189-00-9 30.5 26.5 4.0 - - - - - - - - - -
  0.00(2) 0.42(2) 0.42(2)
Polybutylene terephthalate (PBT) 26062-94-2 46.0 42.0 4.1 47.1 45.8 1.3 0.8 0.6 - - - - -
  0.24(4) 2.83(4) 2.92(4) -(1) -(1) -(1) -(1) -(1)
Polytetramethylene oxide - 31.9 27.4 4.5 - - - - - - - - - -
  -(1) -(1) -(1)
Polyvinyl fluoride (PVF) 24981-14-4 38.6 34.0 4.6 37.5 35.6 1.9 2.8 6.0 - - - - -
  2.85(5) 5.72(5) 4.38(5) 1.30(3) 2.08(3) 0.85(3) 4.73(3) 6.62(3)
Nylon 6,12 24936-74-1 67.0 62.0 4.7 - - - - - - - - - -
  -(1) -(1) -(1)
Polytetrahydrofuran (PTHF) 25190-06-1 31.9 27.2 4.7 - - - - - - - - - -
  0.00(2) 0.28(2) 0.28(2)
Poly iso-butyl methacrylate (PIBMA) 9011-15-8 30.9 26.3 4.7 - - - - - 20.0 18.3 4.9 6.3 9.4
  0.00(2) 0.49(2) 0.49(2) 2.11(3) 0.93(3) 5.12(3) 2.10(3)
Polychloroprene 9010-98-4 43.6 38.8 4.8 - - - - - - - - - -
  0.00(2) 0.14(2) 0.14(2)
Polyvinylidene chloride (PVDC, Saran) 9002-85-1 45.3 40.4 4.9 40.3 40.4 -0.1 0.0 2.6 23.1 19.0 9.6 9.0 5.8
  0.38(4) 2.93(4) 2.91(4) -(1) -(1) -(1) -(1) -(1) 1.98(2) 0.64(2) 1.70(2) 2.62(2)
Polystyrene (PS) 9003-53-6 41.7 37.0 5.0 36.9 37.9 -0.9 0.1 2.2 23.9 22.8 5.8 4.3 12.7
  1.24(8) 3.47(9) 2.84(8) 5.80(3) 4.32(3) 1.68(3) 0.20(3) 2.72(3) -(1) -(1) -(1) -(1)
Poly n-butyl methacrylate (PnBMA) 95608-33-7 32.3 27.3 5.0 - - - - - 18.4 16.0 6.2 6.6 9.5
  1.56(5) 2.59(5) 1.78(5) -(1) -(1) -(1) -(1)
Nylon 12 24937-16-4 38.2 33.1 5.2 41.3 37.0 4.3 0.6 7.6 22.2 18.5 8.1 9.1 6.3
  3.46(2) 3.96(2) 0.42(2) -(1) -(1) -(1) -(1) -(1) -(1) -(1) -(1) -(1)
Polycarbonate (PC) 24936-68-3 43.4 38.2 5.2 - - - - - 22.2 19.6 8.8 5.7 10.2
  8.21(3) 9.24(3) 3.69(3) 1.75(3) 2.58(3) 1.04(3) 4.06(3)
Polyvinyl butyrate - 31.1 25.8 5.3 - - - - - - - - - -
  -(1) -(1) -(1)
Polytrifluoroethylene 24980-67-4 27.5 22.0 5.4 25.4 23.1 2.3 1.8 0.7 - - - - -
  3.65(3) 2.10(3) 3.20(3) -(1) -(1) -(1) -(1) -(1)
Ethylene-propylene-diene-monomer (EPDM) 25038-36-2 35.5 29.7 5.8 - - - - - - - - - -
  -(1) -(1) -(1)
Polymethyl acrylate (PMA) 25087-26-7 41.4 35.6 5.8 - - - - - - - - - -
  0.85(4) 4.12(4) 4.45(4)
Polyetheretherketone (PEEK) 29658-26-2 42.1 36.2 5.9 - - - - - - - - - -
  -(1) -(1) -(1)
Polyethyl acrylate (PEA) 9003-32-1 37.0 30.6 6.4 - - - - - - - - - -
  -(1) -(1) -(1)
Polychlorotrifluoroethylene 9002-83-9 29.5 22.6 6.9 - - - - - 16.5 15.6 2.5 4.7 5.8
  1.78(3) 1.19(3) 2.89(3) 2.10(3) 1.46(3) 2.44(3) 1.56(3)
Polyethersulfone (PES) 25154-01-2 47.0 40.0 7.0 - - - - - 21.0 18.3 8.2 6.4 6.3
  -(1) -(1) -(1) 0.91(6) 3.10(6) 2.33(6) 2.61(6)
Polyethylene terephthalate (PET) 25038-59-9 43.7 36.6 7.2 45.3 42.6 1.8 0.3 3.7 20.8 18.7 6.3 6.7 6.5
  3.42(16) 4.64(16) 3.42(16) 0.78(2) 2.83(2) 0.71(2) 0.21(2) 1.06(2) 1.25(8) 2.03(8) 2.80(8) 3.36(8)
Polyvinyl proprionate 25035-84-1 34.0 26.5 7.5 - - - - - - - - - -
  -(1) -(1) -(1)
Epoxies - 45.0 37.2 7.8 - - - - - 24.1 19.2 10.9 9.6 11.1
  4.63(5) 4.68(5) 7.00(5) 2.53(13) 2.37(13) 2.66(13) 3.98(13)
Polymethyl methacrylate (PMMA, acrylic, plexiglas) 9011-14-7 43.5 35.9 7.8 42.2 41.6 0.6 0.0 11.1 21.3 17.9 10.1 5.4 11.0
  2.88(14) 4.09(13) 3.79(13) 2.97(11) 2.36(11) 0.89(11) 0.04(11) 5.84(11) 1.37(5) 4.46(5) 3.73(5) 4.63(5)
Acrylonitrile butadiene styrene (ABS) 9003-56-9 43.6 35.8 8.0 38.6 39.4 -0.8 0.9 3.7 19.2 17.0 5.7 6.8 9.4
  4.83(5) 2.77(5) 2.55(5) 4.81(2) 0.00(2) 4.88(2) 0.14(2) 2.76(2) 0.92(2) 4.17(2) 0.49(2) 2.19(2)
Polyurethanes - 39.3 30.8 8.6 30.0 30.9 -0.9 0.02 10.0 22.8 18.8 10.0 8.2 9.8
  2.60(8) 3.63(8) 3.95(8) -(1) -(1) -(1) -(1) -(1) 1.53(11) 2.54(11) 3.09(11) 3.48(11)
Polyvinylidene fluoride (PVDF) 24937-79-9 34.4 25.7 8.7 30.5 28.6 1.9 10.5 0.08 23.2 17.0 12.1 10.2 4.1
  4.17(4) 4.64(4) 4.81(4) -(1) -(1) -(1) -(1) -(1) -(1) -(1) -(1) -(1)
Polyimide (PI) 25038-81-7 47.0 38.2 8.8 44.0 42.5 1.5 0.1 6.0 - - - - -
  8.49(2) 16.8(2) 8.27(2) -(1) -(1) -(1) -(1) -(1)
Polyethyl methacrylate (PEMA) 9003-42-3 35.9 26.9 9.0 - - - - - 20.0 17.5 8.5 4.7 9.6
  -(1) -(1) -(1) 1.34(3) 0.62(3) 3.82(3) 1.99(3)
Poly(L-alanine) 25191-17-7 45.2 36.0 9.2 - - - - - - - - - -
  -(1) -(1) -(1)
Aluminum foil (b) 7429-90-5 41.2 31.7 9.5 - - - - - - - - - -
  2.47(2) 0.57(2) 1.91(2)
Nylon 6 (polycaprolactum, aramid 6) 25038-54-4 42.7 33.1 9.6 45.3 42.5 2.8 0.2 9.6 20.3 17.0 3.4 10.6 5.1
  6.08(2) 2.69(2) 3.39(2) -(1) -(1) -(1) -(1) -(1) -(1) -(1) -(1) -(1)
Nylon 6,6 32131-17-2 44.8 36.3 9.8 40.2 36.9 3.3 1.5 12.1 25.8 17.2 9.9 16.5 4.4
  3.07(8) 5.63(9) 4.03(8) 3.61(2) 0.71(2) 2.90(2) 2.11(2) 13.5(2) 1.11 1.10 6.80 1.24
Polyphenylene oxide (PPO) 25134-01-4 46.0 36.0 10.0 - - - - - 20.1 17.9 3.1 8.5 8.6
  -(1) -(1) -(1) -(1) -(1) -(1) -(1)
Cellulose acetate (CA) 9004-35-7 42.0 31.0 11.1 43.5 39.0 4.5 0.3 22.2 23.5 17.1 13.1 9.4 10.6
  5.44(2) 1.84(2) 3.61(2) 6.42(4) 4.20(4) 3.25(4) 0.33(4) 2.71(4) 1.58(4) 4.41(4) 3.81(4) 2.96(4)
Polyethylene oxide (PEO, PEG, polyethylene glycol) 25322-68-3 42.8 30.8 12.1 45.1 44.3 0.8 0.02 58.0 - - - - -
  0.07(2) 0.21(2) 0.14(2) 1.59(4) 1.34(4) 1.60(4) 0.03(4) 10.2(4)
Polyoxymethylene (POM, polyacetal, polymethylene oxide) 24969-26-4 39.0 26.2 12.8 - - - - - - - - - -
  7.99(2) 6.15(2) 1.84(2)
Polybutylene isophthalate - 47.8 34.9 12.9 - - - - - - - - - -
  -(1) -(1) -(1)
Polyvinyl acetate (PVA) 9003-20-7 37.7 24.8 13.0 44.5 42.6 1.9 0.04 22.3 25.7 20.9 11.3 9.7 13.7
  2.89(5) 1.65(5) 1.53(5) -(1) -(1) -(1) -(1) -(1) -(1) -(1) -(1) -(1)
Polypropylene isophthalate - 49.3 35.1 14.2 - - - - - - - - - -
  -(1) -(1) -(1)
Cellophane 9005-81-6 45.4 29.8 15.6 - - - - - 28.5 16.1 18.5 14.5 7.3
  -(1) -(1) -(1) -(1) -(1) -(1) -(1)
Polysulfone (PSU) 25135-51-7 46.6 30.4 16.2 - - - - - 21.5 18.5 8.5 7.0 9.4
  -(1) -(1) -(1) 2.17(3) 2.61(3) 1.12(3) 1.69(3)
2-Hydroxyethyl methacrylate (HEMA, ethylene glycol monoacrylate) 867-77-9 56.8 36.3 20.5 - - - - - - - - - -
  1.20(2) 0.49(2) 0.71(2)
Nylon 4 24938-56-5 48.5 27.8 20.7 - - - - - - - - - -
  -(1) -(1) -(1)
Nylon 2 (polyglycine) 25718-94-9 50.1 27.9 22.2 - - - - - - - - - -
  -(1) -(1) -(1)
Polyacrylamide 9003-05-8 52.3 26.5 25.8 - - - - - - - - - -
  -(1) -(1) -(1)

(a) Atactic PP CAS #9003-08-0; isotactic PP CAS #25085-53-4To top of page

(b) Aluminum foil, while obviously not a polymer, is included due to its widespread use in package converting and other industries.To top of page

(1) Names which are most widely used to describe the material or family of materials (e.g., polyurethanes and epoxies) at hand are preferred here. Commonly used acronyms and synonyms are also shown.To top of page

(2) CAS (Chemical Abstract Series) numbers are shown where available. In a number of instances, more than one CAS number is assigned to a given polymer — in some cases the details and nuances of these divergences are not at all clear. We have tried to reference the CAS number which appears to have the widest use with reference to the solid state properties of the given polymer.To top of page

(3) γs: Total surface free energy in mJ/m2 (equivalent to dynes/cm), as reported in polar/dispersion analyses.To top of page

(4) γsd: Dispersion component of surface free energy in mJ/m2 (equivalent to dynes/cm), as reported in polar/dispersion analyses.To top of page

(5) γsp: Polar component of surface free energy in mJ/m2 (equivalent to dynes/cm), as reported in polar/dispersion analyses.To top of page

(6) γs: Total surface free energy in mJ/m2 (equivalent to dynes/cm), as reported in acid—base analyses.To top of page

(7) γsLW: Lipschitz—van der Waals (non-polar) component of surface free energy in mJ/m2 (equivalent to dynes/cm), as reported in acid—base analyses.To top of page

(8) γsAB: Lewis acid—base interaction component of surface free energy in mJ/m2 (equivalent to dynes/cm), as reported in acid—base analyses.To top of page

(9) γs-: Base polarity (electron-donor) component of surface free energy in mJ/m2 (equivalent to dynes/cm), as reported in acid—base analyses.To top of page

(10) γs+: Acid polarity (electron-acceptor) component of surface free energy in mJ/m2 (equivalent to dynes/cm), as reported in acid—base analyses. To top of page

(11) δ: Total Hansen solubility parameter (square root of the sum of squares of the average values for dispersion, polar, and hydrogen bonding components), in MPa1/2 (equivalent to joules/cubic centimeter; 2.0455 x (cal/cc)1/2) @ 20-25oC (293.15-298.15 K). All data from Hansen Solubility Parameters: A User's Handbook, 2nd Ed., C.M. Hansen, CRC Press, Boca Raton, FL, 2007.To top of page

(12) δD: Hansen dispersion solubility parameter, in MPa1/2 (equivalent to joules/cubic centimeter; 2.0455 x (cal/cc)1/2) @ 20-25oC (293.15-298.15 K). All data from Hansen Solubility Parameters: A User's Handbook, 2nd Ed., C.M. Hansen, CRC Press, Boca Raton, FL, 2007.To top of page

(13) δP: Hansen polar solubility parameter, in MPa1/2 (equivalent to joules/cubic centimeter; 2.0455 x (cal/cc)1/2) @ 20-25oC (293.15-298.15 K). All data from Hansen Solubility Parameters: A User's Handbook, 2nd Ed., C.M. Hansen, CRC Press, Boca Raton, FL, 2007.To top of page

(14) δH: Hansen hydrogen bonding solubility parameter, in MPa1/2 (equivalent to joules/cubic centimeter; 2.0455 x (cal/cc)1/2) @ 20-25oC (293.15-298.15 K). All data from Hansen Solubility Parameters: A User's Handbook, 2nd Ed., C.M. Hansen, CRC Press, Boca Raton, FL, 2007.To top of page

(15) Ro: Interaction radius. All data from Hansen Solubility Parameters: A User's Handbook, 2nd Ed., C.M. Hansen, CRC Press, Boca Raton, FL, 2007.To top of page